Bego Bellavest
Description
Quantity: 144 x 90g bags
The precision crown and bridge investment material Bellavest® SH offers outstanding versatility and flexibility
• Appointments can be coordinated with ease because Bellavest® SH can either be preheated rapidly, with an insertion temperature of up to 900°C, or conventionally
• Phosphate-bonded precision casting investment material offers reliable, simple handling along with optimal parameters of use
• Simple to use with the special mixing liquid BegoSol® HE for maximum flexibility in conjunction with just a single liquid
• Precise expansion control and fine, creamy consistency for reliable processing and reproducible quality for a range of indications, from press able ceramics to telescopic crowns made from non-precious alloys
• Long working time of 5 minutes enables reliable, fatigue-free working
• Extremely smooth cast surfaces make for a good accuracy of fit and time savings due to minimal finishing times
• Cures with a high edge-strength, yet still permits easy deflasking. For the user, this means time savings and economical use of blasting materials Korox®
Physical data
Mixing liquid - BegoSol® HE
Processing time at 20 °C - approx. 4.5- 5 minutes
Shelf life in unopened bag - 24 months
Characteristic values of the material according to DIN EN ISO 15912
Beginning of solidification (Vicat time) - approx. 10 minutes
Compressive strength after 2 hours [MPa] - 4.2- 5.1
Linear thermal expansion [%] - 0.85
Instructions for using Bellavest® SH:
Universal investment materials are characterised by adjustable expansion levels and resistance to temperature and pressure.
Bellavest® SH combines all the requirements for crown and bridge work. This applies equally to precious-metal and non-precious alloys, and also includes pressable ceramics. With BegoSol® HE the desired expansion can be adjusted for every application and indication. This makes Bellavest® SH one of the world%u2018s leading crown and bridge investment materials. It is best to use Bellavest
® SH and BegoSol® HE at a constant temperature of 20°C and processing parameters, such as mixing time and mixing speed, should also be constantly maintained to ensure consistent.
Tips for application
• The higher the concentration of BegoSol®, the greater the expansion of the investment material
• Lowering the concentration reduces the level of expansion
• Uniform parameters of use are essential for achieving reproducible casting results
Bego Bellavest SH Information Sheet.pdf